The results show that fatigue, creep and oxidation damage always develops simultaneously during low cycle fatigue at high temperature.

试样的微观断口分析显示了在高温应变疲劳试验中同时存在疲劳、蠕变和氧化损伤。

However, cracks initialized in the diffusion layer between substrate and bond coat when TBCs were tested with low cycle fatigue at high temperature.

而在高温低周疲劳条件下裂纹是在粘结层与高温合金基体的扩散层处。

High temperature low cycle fatigue (HLF) life prediction models have great significance for design of high temperature structure under cycLic loading.

高温低周疲劳(HLF)寿命预测方法对于承受变幅载荷的高温构件的设计具有重要意义。

The high temperature wearing was due to the fatigue delamination of the oxide, the lump wear debris were revealed on the precision cast steel, and the bar wear debris on H13 steel.

高温磨损机理为氧化物疲劳剥落磨损，精铸热锻模具钢磨损磨屑为厚大块状，而H13钢磨损磨屑以条状为主。

The multiaxial cyclic characteristic of GH4169 was investigated for the thin tubular multiaxial fatigue specimen under proportional and non-proportional loading at high temperature.

薄壁疲劳试，控制应扭循环温合金材GH4169循环特性试验研究。

High core temperature has been shown to impair the ability to maintain muscle activation, and this impairment is associated with central fatigue.

体核温度过高会对肌肉运动能力造成损害，这与中枢疲劳有关。